A novel high‐contrast ratio electrochromic material from spiro[cyclododecane‐1,9′‐fluorene]bicarbazole
Makaleler > Tam Makale · 2010
Yazarlar: Ozlem Usluer, Sermet Koyuncu, Serafettin Demic, René A. J. Janssen
Journal of Polymer Science Part B: Polymer Physics, Uluslararası, Wos, 2010, cilt 49, ss 333-341
DOI: 10.1002/polb.22190
Özet
Abstract A novel electroactive spirocyclododecylfluorene monomer named 2,7‐bis(carbazol‐9‐yl)‐9,9′‐spiro[cyclododecane‐1,9′‐fluorene] (SFC) was synthesized and electrochemically polymerized to give a very stable multi‐electrochromic polymer (poly‐SFC). Two separate oxidation processes were observed for both SFC monomer and poly‐SFC that carries two carbazole units. The polymeric film of poly‐SFC was coated onto ITO/glass surface, and it shows different colors (transparent, yellowish green, green, and dark green) upon stepwise oxidations. An electrochromic device based on poly‐SFC was assembled in the sandwich cell configuration of ITO/poly‐SFC//gel electrolyte//PEDOT/ITO. Poly‐SFC exhibits 90% of transparency at neutral state and a high contrast ratio (ΔT = 58% at 800 nm). This device constructed from it represents a response time of about 1 s, high coloration efficiency (1377 cm2 C–1) and retained its performance by 96.4% even after 1000 cycles. Exhibiting high transparency at neutral state, reversible redox behavior, resistance to overoxidation, and especially high contrast ratio at near IR region can make poly‐SFC be useful and promising candidate for electrochromic applications despite having a relatively slow response time. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys, 2010