Electromechanical characterization of multilayer graphene-reinforced cellulose composite containing 1-ethyl-3-methylimidazolium diethylphosphonate ionic liquid
Makaleler > Tam Makale · 2017
Yazarlar: Emine Akar, Yoldas Seki, Okan Ozdemir, Ibrahim Sen, Mehmet SARIKANAT, Barış Oğuz GÜRSES, Ozgun Cem Yilmaz, Levent Cetin, Kutlay Sever
SCIENCE AND ENGINEERING OF COMPOSITE MATERIALS, SCI Expanded İndekslerine Giren Dergi, Uluslararası, 2017, cilt 24, ss 289-295
Özet
In this study, multilayer graphene (Gr)-reinforced cellulose composites were synthesized by using 1-ethyl-3-methylimidazolium diethylphosphonate ionic liquid. The composites were fabricated via dissolving the cellulose in 1-ethyl-3-methylimidazolium diethylphosphonate and Gr loading at different ratios (0.2, 0.4, and 0.6 wt.%). Both sides of the composites were coated with gold leaf to generate electrodes. The effect of Gr loading on chemical functional groups, crystallographic properties, thermal stability, and morphological and mechanical properties of cellulose film was investigated by Fourier transform infrared spectroscopy, X-ray diffraction, thermogravimetric analysis, scanning electron microscopy, and tensile test, respectively. Electromechanical behavior of the cellulose composite films reinforced with Gr (0.2, 0.4, and 0.6 wt.%) was investigated under DC excitation voltages of 1, 3, 5 and 7 V. Gr loading of 0.2 wt.% increased maximum tip displacement by 400% when the actuator is excited with 3 V.