Reversal of reduced bond strength after bleaching.
Makaleler > Tam Makale · 2010
Yazarlar: M Erhan Comlekoglu, Bulent Gokce, Aysegul Demirbas Kaya, Lezize Şebnem TÜRKÜN, Birgul Ozpinar
General dentistry, Uluslararası, 2010, cilt 58, ss 258-
Özet
This article investigated how the shear bond strength of a luting resin to dentin was affected by antioxidant treatment and delayed bonding after bleaching with carbamide peroxide. Using a lowspeed diamond saw, 40 flat dentin surfaces were prepared from freshly extracted human molars and divided into three bleaching groups (n = 10) and a control group (n = 10). Group 1 consisted of specimens bonded immediately after bleaching. Group 2 specimens were treated with an antioxidant agent (10% sodium ascorbate), while Group 3 specimens were immersed in artificial saliva for one week after bleaching. Specimens in Group 4 were not bleached but were immersed in artificial saliva for one week before bonding. Forty ceramic blocks were prepared and luted to teeth using a dual-curing resin cement. The specimens were thermocycled and the shear bond strength tests were performed using a universal testing machine. Fracture analysis was performed using a scanning electron microscope. While the Group 1 samples demonstrated the lowest shear bond strengths (11.9 +/- 3 MPa) (p < 0.05), no significant differences were found among samples in Group 2 (26.3 +/- 7.1 MPa), Group 3 (20.7 +/- 6.5 MPa), and Group 4 (22.1 +/- 2.5 MPa) (p = 0.05).